| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 比重 |
| ASTM D-792 | 1.62 |
|
| 模具收缩率 | 1.6mm(0.063in) | ASTM D-955 | -0.1 | % |
| 机械性能 | 弯曲模量 | 1.6mm(0.063in),23℃(73℉) | ASTM D-790 | 14000 | MPa |
| IZOD冲击强度 | 3.2mm(0.125in),23℃(73℉) | ASTM D-256 | 225 | J/m |
| 拉伸强度 | 1.6mm(0.063in),23℃(73℉) | ASTM D-638 | 173 | MPa |
| 拉伸模量 | 1.6mm(0.063in),23℃(73℉) | ASTM D-638 | 19306 | MPa |
| IZOD冲击强度 | 1.6mm(0.063in),23℃(73℉) | ASTM D-256 | 170 | J/m |
| 拉伸强度 | 3.2mm(0.125in),23℃(73℉) | ASTM D-638 | 150 | MPa |
| 弯曲强度 | 0.8mm(0.032in),23℃(73℉) | ASTM D-790 | 215 | MPa |
| 无缺口冲击强度 | 3.2mm(0.125in),23℃(73℉) | ASTM D-4812 | 740，20%NB | J/m |
| 弯曲模量 | 0.8mm(0.032in),23℃(73℉) | ASTM D-790 | 18000 | MPa |
| 弯曲强度 | 3.2mm(0.125in),23℃(73℉) | ASTM D-790 | 183 | MPa |
| 压缩强度 | 3.2mm(0.125in) | ASTM D-695 | 89 | MPa |
| 断裂伸长率 | 1.6mm(0.063in),23℃(73℉) | ASTM D-638 | 1.6 | % |
| 弯曲模量 | 3.2mm(0.125in),23℃(73℉) | ASTM D-790 | 13100 | MPa |
| IZOD冲击强度 | 0.8mm(0.032in),23℃(73℉) | ASTM D-256 | 400,40%NB | J/m |
| 剪切强度 | 0.8mm(0.032in) | ASTM D-732 | 57 | MPa |
| 弯曲强度 | 1.6mm(0.063in),23℃(73℉) | ASTM D-790 | 192 | MPa |
| 断裂伸长率 | 3.2mm(0.125in) | ASTM D-638 | 1.7 | % |
| 无缺口冲击强度 | 1.6mm(0.063in),23℃(73℉) | ASTM D-4812 | 840 | J/m |
| 洛氏硬度 |
| ASTM D-785 | 63 |
|
| 拉伸模量 | 3.2mm(0.125in),23℃(73℉) | ASTM D-638 | 18000 | MPa |
| 压缩模量 | 3.2mm(0.125in) | ASTM D-695 | 5300 | MPa |
| 剪切强度 | 3.2mm(0.125in) | ASTM D-732 | 58 | MPa |
| 无缺口冲击强度 | 0.8mm(0.032in),23℃(73℉) | ASTM D-4812 | NB | J/m |
| 电气性能 | 损耗因数 | 3.2mm(0.125in),23℃(73℉) | ASTM D-2520 B | 0.004 |
|
| 介电常数 | 3.2mm(0.125in),23℃(73℉) | ASTM D-2520 B | 4.3 |
|
| 损耗因数 | 3.2mm(0.125in),23℃(73℉) | ASTM D-150 | 0.029 |
|
| 介电常数 | 3.2mm(0.125in),23℃(73℉) | ASTM D-150 | 3.8 |
|
| 介电常数 | 0.8mm(0.032in),23℃(73℉) | ASTM D-150 | 3.5 |
|
| 介电常数 | 0.8mm(0.032in),23℃(73℉) | ASTM D-2520 B | 4.4 |
|
| 损耗因数 | 3.2mm(0.125in),23℃(73℉) | ASTM D-150 | 0.013 |
|
| 损耗因数 | 0.8mm(0.032in),23℃(73℉) | ASTM D-150 | 0.029 |
|
| 介电常数 | 1.6mm(0.063in),23℃(73℉) | ASTM D-2520 B | 4.3 |
|
| 表面电阻率 |
| ASTM D-257 | 1×1015 | Ohm |
| 介电常数 | 0.8mm(0.032in),23℃(73℉) | ASTM D-150 | 3.9 |
|
| 介电常数 | 3.2mm(0.125in),23℃(73℉) | ASTM D-150 | 4.3 |
|
| 体积电阻率 |
| ASTM D-257 | 1×1016 | Ohm-cm |
| 介电强度 | 3.2mm,23℃(73℉) | ASTM D-149 | >28 | Kv/mm |
| 损耗因数 | 1.6mm(0.063in),23℃(73℉) | ASTM D-2520 B | 0.004 |
|
| 介电强度 | 1.6mm,23℃(73℉) | ASTM D-149 | 35 | Kv/mm |
| 损耗因数 | 0.8mm(0.032in),23℃(73℉) | ASTM D-150 | 0.013 |
|
| 损耗因数 | 0.8mm(0.032in),23℃(73℉) | ASTM D-2520 B | 0.004 |
|
| 介电强度 | 1.6mm(0.063in) | ASTM D-149 | 31 | Kv/mm |
| 热性能 | 表面电阻率 |
| ASTM D-257 | 1×1015 | Ohm |
| 熔点 |
| ASTM D-3418 | 352 | ℃ |
| 解链温度范围 |
|
| 363-371 | ℃ |
| 热导率 |
| ASTM C-177 | 0.32 | W/mk |
| 模压温度范围 |
|
| 30-95 | ℃ |
| 玻璃化转变温度 |
| ASTM D-3418 | 120 | ℃ |
| 干燥温度 |
|
| 135 | ℃ |
| 热变形温度 | 1.80MPa | ASTM D-648 | 289 | ℃ |
| 其它性能 | RTI,Mechanical with Impact | 1.5mm | UL 746-B | 210 | ℃ |
| RTI,Electrical | 3.0mm | UL 746-B | 240 | ℃ |
| RTI,Mechanical without Impact | 1.5mm | UL 746-B | 240 | ℃ |
| RTI,Electrical | 0.75mm | UL 746-B | 240 | ℃ |
| RTI,Mechanical without Impact | 0.75mm | UL 746-B | 240 | ℃ |
| RTI,Mechanical with Impact | 3.0mm | UL 746-B | 210 | ℃ |
| RTI,Mechanical without Impact | 3.0mm | UL 746-B | 240 | ℃ |
| RTI,Electrical | 1.5mm | UL 746-B | 240 | ℃
|