生产企业： 意大利兰蒂奇
| 规格级别 | 其它 其它 注塑 | 外观颜色 | |
|---|---|---|---|
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | ASTM D-570 | 1.3-0.2 | % | |
| 饱和吸水率 | ASTM D-570 | 8.5±0.5 | % | ||
| 熔点 | ASTM D-648 | 254 | ℃ | ||
| 密度 | ASTM D-792 | 1.14 | g/cm3 | ||
| 物理性能 | 阻燃性 | UL 94 | V2/1.5mm | Class/mm | |
| 机械性能 | 弯曲模量 | C | ASTM D-790 | 1200 | MPa |
| 断裂伸长率 | D | ASTM D-638 | 50-60 | % | |
| 弯曲强度 | D | ASTM D-790 | 115 | MPa | |
| 冲击强度 | C | ASTM D-256 | 不断裂 | J/M | |
| 弯曲强度 | C | ASTM D-790 | 55 | MPa | |
| 冲击强度 | D | ASTM D-256 | 30 | J/M | |
| 弯曲模量 | D | ASTM D-790 | 2800 | MPa | |
| 洛氏硬度 | D | ASTM D-785 | R118 | ||
| 拉伸强度 | D | ASTM D-638 | 85 | MPa | |
| 拉伸强度 | C | ASTM D-638 | 60 | MPa | |
| 断裂伸长率 | C | ASTM D-638 | 100 | % | |
| 冲击强度（缺） | D | ASTM D-256 | 45 | J/M | |
| 蠕变模量 | C | DIN 53444 | 350 | N/mm2 | |
| 冲击强度 | D | ASTM D-256 | 110 | J/M | |
| 电气性能 | 表面电阻 | C | ASTM D-257 | 1013 | Ω |
| 介电常数 | D | ASTM D-696 | 3.5 | ||
| 体积电阻 | C | ASTM D-149 | 1012 | Ω.cm | |
| 表面电阻 | D | ASTM D-257 | 1013 | Ω | |
| 介电损耗角 | D | ASTM D-150 | 0.025 | ||
| 体积电阻 | D | ASTM D-149 | 1015 | Ω.cm | |
| 介电损耗角 | C | ASTM D-150 | 0.2 | ||
| 介电强度 | C | ASTM D-150 | 80 | KV/mm | |
| 介电强度 | D | ASTM D-150 | 120 | KV/mm | |
| 热性能 | 热变形温度 | 66PSi | ASTM D-785 | >220 | ℃ |
| 线性热膨胀系数 | D | ASTM D-214 | 7-10 | I/K10-5 | |
| 热变形温度 | 264PSi | ASTM D-785 | 100 | ℃ | |